ANALISA SIFAT FISIK DAN KIMIA BRIKET ARANG DARI CAMPURAN TANDAN KOSONG AREN (Arenga pinnata Merr) DAN CANGKANG KEMIRI (Aleurites trisperma)

Analysis Of Physical Properties and Chemical Charcoal Bricets from ArenEmbassy (Arenga pinnata Merr) And Pecan Shell (Aleurites trisperma)

Hari Wahyu Basuki, Yuniarti, Dan Fatriani

Jurusan Kehutanan

Fakultas Kehutanan Universitas Lambung Mangkurat

ABSTRACT waste the shell of hazelnut and empty fruit palm has a considerable
potential and can be used as raw material of charcoal briquette. This research aims to
analyse the charcoal  properties of a mixture of hazelnut shells with empty bunks of palm over
chemical physical  properties of the resulting charcoal briquettes. To know the effect of charcoal
briquettes mixed with hazelnut shell and empty palm,
carried out treatment 100% hazelnut shell, 100% palm empty  bunch, 75% hazelnut shell + 25% empty palm bunch, 75% bunches empty palm + 25%
hazelnut shell, 50% shell Hazelnut + 50% palm
empty bunch, adhesive used is tapioca flour. The water  content of charcoal briquettes ranging from 7.568%-11.734%, density 0,
520g/cm³-0, 604g/cm³, average ash content of 15%-22.666%, flying substance rate 43.666%-52%, carbon
bonded range between 17.335%-44.098%, and the Calor
value of 3676, 86kal /g-4749, 606cal/G. Water content that meets ASTM in Treatment A (100%
hazelnut case) of 7.568%, other treatment does not meet ASTM standards. Density, ash content,
flying substance levels, bonded carbon and calor value resulting from a variety of no-existing
treatments that meet the standards.

Keywords: palm briquettes charcoal Blanks, candlenut briquette, influence of physical and 
chemical properties, ASTM standard

ABSTRAK Limbah cangkang kemiri dan tandan kosong aren memiliki potensi cukup besar dan dapat digunakan sebagai bahan baku briket arang. Penelitian ini bertujuan untuk menganalisis sifat arang dari campuran cangkang kemiri dengan tandan kosong aren terhadap sifat fisik kimia briket arang yang dihasilkan. Untuk mengetahui pengaruh briket campuran arang cangkang kemiri dan tandan kosong aren, dilakukan perlakuan 100% cangkang kemiri, 100% tandan kosong aren, 75% cangkang kemiri + 25% tandan kosong aren, 75% tandan kosong aren + 25% cangkang kemiri, 50% cangkang kemiri + 50% tandan kosong aren, perekat yang di gunakan adalah tepung tapioka. Briket arang yang dihasilkan kadar air berkisar antara 7,568% - 11,734%, kerapatan 0,520g/cm³ - 0,604g/cm³, kadar abu rata-rata berkisaran 15% - 22,666%, kadar zat terbang 43,666% - 52%, karbon terikat berkisar antara 17,335% - 44,098%, dan nilai kalor 3676,86kal/g - 4749,606kal/g. Kadar air yang memenuhi ASTM terdapat pada perlakuan A (100% cangkang kemiri) sebesar 7,568%, perlakuan lainnya tidak memenuhi standar ASTM. Kerapatan, kadar abu, kadar zat terbang, karbon terikat dan nilai kalor yang dihasilkan dari berbagai perlakuan tidak ada yang memenuhi standar.