ABSTRACT. This study aimed to analyze the combustion rate of candlenut shell (Aleurites moluccanus) charcoal briquettes using sago adhesive through moisture content, calorific value, and ash content tests. The research was conducted in February 2025 at the Workshop of the Faculty of Forestry, Universitas Lambung Mangkurat, and Forestchem Banjarbaru. This study employed a Completely Randomized Design (CRD) with four treatments and three replications using sago adhesive concentrations of 5%, 10%, 15%, and 20%, resulting in a total of 12 briquette samples. The results showed that briquettes with higher adhesive concentrations produced lower combustion rates, with the lowest average value of 0.392 g/minute, while lower adhesive concentrations produced higher combustion rates of 0.842 g/minute. The lowest moisture content was 5.111%, while the highest was 7.154%. The calorific value ranged from 3,384 cal/g to 5,233 cal/g. The highest ash content was 5.206%, while the lowest was 4.833%. These findings indicate that the proportion of sago adhesive significantly affects the combustion characteristics and quality of candlenut shell charcoal briquettes.

Keywords: Charcoal Briquettes; Candlenut Shell; Sago Adhesive; Combustion Rate.

ABSTRAK. Penelitian ini bertujuan untuk menghitung l~aju$ pembakaran briket arang cangkang kemiri (Aleurites moluccanus) dengan bahan perekat sagu melalui uji kadar air, nilai kalor,  dan kadar abu. Penelitian ini dilaksanakan pada bulan Februari 2025 di Workshop Fakultas Kehutanan Universitas Lambung Mangkurat dan Forestchem Kota Banjarbaru. penelitian ini menggunakan metode Rancangan Acak Lengkap (RAL) 4 perlakuan dan 3 pengulangan dengan perekat sagu konsentrasi 5%, 10%, 15%, dan 20% total sampel briket yang diteliti sebanyak 12 sampel. Hasil penelitian ini menunjukkan briket dengan konsentrasi perekat yang banyak menghasilkan nilai rata-rata pada uji yang sangat rendah berkisar 0,392 g/menit sedangkan konsentrasi perekat yang sedkit menghasilkan laju pembakaran tinggi berkisar 0,842 g/menit. Nilai kadar air terendah dengan nilai rata-rata 5,111% dan nilai tertinggi dengan rata-rata 7,154%. Nilai kalor dengan nilai terendah rata--rata 3,384 kal/g sedangkan nilai kalor tertinggi berkisar 5,233 kal/g, nilai kadar abu tertinggi rata-rata 5,206% sedangkan nilai kadar abu terendah dengan rata-rata 4,833%. Temuan ini menunjukkan bahwa proporsi perekat sagu secara signifikan memengaruhi karakteristik pembakaran dan kualitas briket arang tempurung kemiri.

Kata kunci: Briket Arang; Cangkang Kemiri; Perekat Sagu; Laju Pembakaran.